We use the ABS-V0 material in the following processes:
- plastic injection moulding
- thermoplastic structure foaming (TSF)
ABS-V0 Material Datascheet:
特性Property | 测试方法Test Method | 测试条件Test Condition | 单位Unit | 防火注塑级ABS |
---|---|---|---|---|
引张强度Tensile Strength | ASTM D638 | 1/8", 6 mm/min. | Kg/cm² | 400 |
延伸率Tensile Elongation | ASTM D638 | 1/8", 6 mm/min. | % | 25 |
弯曲强度Flexural Strength | ASTM D790 | 1/4", 2.8 mm/min. | Kg/cm² | 650 |
弯曲弹性率Flexural Modulus | ASTM D790 | 1/4", 2.8 mm/min. | Kg/cm² | 24000 |
IZOD冲击强度IZOD Impact Strength | ASTM D256(Notched) | 1/4", 23°C 1/8", 23°C | Kg-cm/cm Kg-cm/cm | 22 25 |
流动系数Melt Flow Index | ASTM D1238 | 200°C, 10 Kg | g/10min | 4.2 |
硬度Hardness | ASTM D785 | 1/2" | R Scale | 102 |
密度Density | ASTM D792 | 23°C | g/cm³ | 1.16 |
软化点Vicat Softening Temp. | ASTM D1525 | 1/8", 50 °C/ hr | °C | 92 |
热变形温度H.D.TAnnealed(85°C, 8hr ) Unannealed | ASTM D648 | 1/4", 120 °C/ hr | °C | 85 76 |
燃烧率Flammability | UL94 | – | – | 2.5 mm, V0 3.2 mm 5VA |