We use the PA6 material in the following processes：
- plastic injection moulding
- thermoplastic structure foaming (TSF)
PA6 Material Datasheet:
| 特性 Property | 测试方法 Test Method | 测试条件Test Condition | 单位Unit | 一般注塑级PA6 |
|---|---|---|---|---|
| 引张强度 Tensile Strength | ISO 527 | 50 mm/min. | MPa | 86 |
| 断裂伸长率 Elongation at Break | ISO 527 | 50 mm/min. | % | 3.9 |
| 弯曲强度 Flexural Strength | ISO 178 | 2 mm/min. | MPa | 92 |
| 弯曲弹性率 Flexural Modulus | ISO 178 | 2 mm/min. | MPa | 2318 |
| 简支梁缺口冲击强度 Charpy Impact notched | ISO 179 | – | KJ/m² | 6.8 |
| 简支梁无缺口冲击强度 Charpy Impact Unotched | ISO 179 | – | KJ/m² | NB |
| 洛氏硬度 Rockwell Hardness | ISO 2039/2 | – | – | 116 |
| 密度 Density | ISO 1183 | 23 °C | g/cm³ | 1.13 |
| 熔点 Melting Point | ISO 3146C | – | °C | 220 |
| 热变形温度H.D.T Annealed Unannealed | ISO 75 | 0.45 MPa 1.81 MPa | °C | – 65 |
| 燃烧率 Flammability | UL94 | – | – | HB |