We use the PA66 GF25material in the following processes：
- plastic injection moulding
- thermoplastic structure foaming (TSF)
PA66 GF25 Material Datasheet:
| 特性Property | 测试方法Test Method | 测试条件Test Condition | 单位Unit | 注塑级增强PA66 GF25 |
|---|---|---|---|---|
| 引张强度Tensile Strength | ISO 527 | 50 mm/min. | MPa | 165 |
| 断裂伸长率Elongation at Break | ISO 527 | 50 mm/min. | % | 3.0 |
| 弯曲强度Flexural Strength | ISO 178 | 2 mm/min. | MPa | 240 |
| 弯曲弹性率Flexural Modulus | ISO 178 | 2 mm/min. | MPa | 7290 |
| 简支梁缺口冲击强度Charpy Impact notched | ISO 179 | – | KJ/m² | 11.1 |
| 简支梁无缺口冲击强度Charpy Impact Unotched | ISO 179 | – | KJ/m² | 68.6 |
| 洛氏硬度Rockwell Hardness | ISO 2039/2 | – | – | 119 |
| 密度Density | ISO 1183 | 23 °C | g/cm³ | 1.32 |
| 熔点Melting Point | ISO 3146C | – | °C | 260 |
| 热变形温度H.D.TAnnealed Unannealed | ISO 75 | 0.45 MPa 1.81 MPa | °C | – 252.3 |
| 燃烧率Flammability | UL94 | – | – | HB |