PA6 GF40

PA6 GF40

We use the PA6 GF40 material in the following processes:

  • plastic injection moulding
  • thermoplastic structure foaming (TSF)

PA6 GF40 Material Datasheet:

特性Property 测试方法Test Method 测试条件Test Condition 单位Unit 增强尼龙PA6 GF40
引张强度Tensile Strength ISO 527
50 mm/min.
MPa
189
断裂伸长率Elongation at Break ISO 527
50 mm/min.
%
3.0
弯曲强度Flexural Strength ISO 178
2 mm/min.
MPa
279
弯曲弹性率Flexural Modulus ISO 178
2 mm/min.
MPa
10692
简支梁缺口冲击强度Charpy Impact notched ISO 179

KJ/m²

16.1

简支梁无缺口冲击强度Charpy Impact Unotched ISO 179
KJ/m²
95
洛氏硬度Rockwell Hardness ISO 2039/2
117
密度Density ISO 1183
23 °C
g/cm³
1.45
熔点Melting Point ISO 3146C
°C
220
热变形温度H.D.TAnnealed Unannealed ISO 75
0.45 MPa 1.81 MPa
°C

211

燃烧率Flammability UL94
HB