We use the PA6 GF50 material in the following processes：
- plastic injection moulding
- thermoplastic structure foaming (TSF)
PA6 GF50 Material Datasheet:
| 特性 Property | 测试方法 Test Method | 测试条件 Test Condition | 单位 Unit | 增强尼龙 PA6 GF50 |
|---|---|---|---|---|
| 引张强度 Tensile Strength | ISO 527 | 50 mm/min. | MPa | 216 |
| 断裂伸长率 Elongation at Break | ISO 527 | 50 mm/min. | % | 2.9 |
| 弯曲强度 Flexural Strength | ISO 178 | 2 mm/min. | MPa | 326 |
| 弯曲弹性率 Flexural Modulus | ISO 178 | 2 mm/min. | MPa | 13582 |
| 简支梁缺口冲击强度 Charpy Impact notched | ISO 179 | – | KJ/m² | 1.9 |
| 简支梁无缺口冲击强度 Charpy Impact Unotched | ISO 179 | – | KJ/m² | 96 |
| 洛氏硬度 Rockwell Hardness | ISO 2039/2 | – | – | 118 |
| 密度 Density | ISO 1183 | 23 °C | g/cm³ | 1.56 |
| 熔点 Melting Point | ISO 3146C | – | °C | 220 |
| 热变形温度H.D.T Annealed Unannealed | ISO 75 | 0.45 MPa 1.81 MPa | °C | – 218 |
| 燃烧率 Flammability | UL94 | – | – | HB |