We use the PC+ABS material in the following processes:
- plastic injection moulding
- thermoplastic structure foaming (TSF)
PC+ABS Material Datasheet:
特性Property | 测试方法Test Method | 测试条件Test Condition | 单位Unit | 一般注塑级PC+ABS |
---|---|---|---|---|
引张强度Tensile Strength | ASTM D638 | 1/8", 6 mm/min. | Kg/cm² | 500 |
延伸率Tensile Elongation | ASTM D638 | 1/8", 6 mm/min. | % | 85 |
弯曲强度Flexural Strength | ASTM D790 | 1/4", 2.8 mm/min. | Kg/cm² | 750 |
弯曲弹性率Flexural Modulus | ASTM D790 | 1/4", 2.8 mm/min. | Kg/cm² | 23000 |
IZOD冲击强度IZOD Impact Strength | ASTM D256(Notched) | 1/4", 23°C 1/8", 23°C | Kg-cm/cm Kg-cm/cm | – 49 |
流动系数Melt Flow Index | ASTM D1238 | 200°C, 5 Kg | g/10min | – |
硬度Hardness | ASTM D785 | 1/2" | R Scale | 108 |
密度Density | ASTM D792 | 23°C | g/cm³ | 1.10 |
软化点Vicat Softening Temp. | ASTM D1525 | 1 Kg, 50 °C/ hr | °C | 125 |
热变形温度H.D.TAnnealed(85°C, 8hr ) Unannealed | ASTM D648 | 18.5 Kg, 120 °C/ hr | °C | 95 |
燃烧率Flammability | UL94 | – | – | HB |