We use the PC V0 material in the following processes:
- plastic injection moulding
- thermoplastic structure foaming (TSF)
PC V0 Material Datasheet:
特性Property | 测试方法Test Method | 测试条件Test Condition | 单位Unit | 阻燃注塑级PC V0 |
---|---|---|---|---|
引张强度Tensile Strength | ISO 527 | – | MPa | 63 |
延伸率Tensile Elongation | ASTM D638 | 1/8", 6 mm/min. | % | 6 |
弯曲强度Flexural Strength | ASTM D790 | 1/4", 2.8 mm/min. | Kg/cm² | 920 |
弯曲弹性率Flexural Modulus | ASTM D790 | 1/4", 2.8 mm/min. | Kg/cm² | 24000 |
IZOD冲击强度IZOD Impact Strength | ASTM D256(Notched) | 1/8", 23°C | Kg-cm/cm | 87 |
流动系数Melt Flow Index | ASTM D1238 | 300°C, 1.2 Kg | g/10min | 10 |
洛氏硬度Rockwell Hardness | ASTM D785 | M Scale | 77 | |
密度Density | ASTM D792 | 23°C | g/cm³ | 1.2 |
软化点Vicat Softening Temp. | ASTM D1525 | 1 Kg, 50 °C/ hr | °C | 150 |
热变形温度H.D.TAnnealed(85°C, 8hr ) Unannealed | ASTM D648 | 4.6 Kg/cm² , 120 °C/ hr 18.6 Kg/cm³, 120 °C/hr | °C | 136 125 |
浊度Haze | ASTM D1103 | 3.2 mm thick | % | <0.8 |
全光穿透率Light Transmission | ASTM D1003 | 3 mm thick | % | 89 |
燃烧率Flammability | UL94 | 2.5 mm | – | V0 |